BILT HAMBER ELECTROX STEEL CORROSION PROTECTOR 1000ML
CarCare24.eu - BHELEC1000, Bilt Hamber Electrox protects steel from corrosion with both barrier and electrical functionality. Coating steel with electrox produces a surface film containing over 90% metallic zinc. Once cured, the tightly packed zinc particles establish an electronically conductive pathway, enabling cathodic protection of the underlying steel, exactly the same principle utilised in hot zinc galvanising.
Why buy this product
Provides class-leading corrosion protection
Protects by cathodic action
Contains more than 90% zinc in dry film
Easy to use single pack material
Easily top coated with wide range of finishes
Self-healing if damaged
Can be left uncoated - max protection achieved when top coated,
Can be brushed or sprayed
Available in aerosol
About this product
Electrox protects steel from corrosion with both barrier and electrical functionality. Coating steel with electrox produces a surface film containing over 90% metallic zinc. Once cured, the tightly packed zinc particles establish an electronically conductive pathway, enabling cathodic protection of the underlying steel, exactly the same principle utilised in hot zinc galvanising.
For years galvanised steel has proven to provide outstanding longevity even in the most hostile and aggressive environments. It’s unfortunate that the process involves hot dipping steel into a bath of liquid zinc.
For many items and projects this is, of course, simply not possible. For those wanting to provide the very best protection to steel, Bilt-Hamber’s electrox allows the advantages of a zinc coating to be obtained as simply as if a normal metal primer were being used. It can be applied by brush or by spra, and as it’s a single pack product there’s no need for mixing activators. The cured zinc film can be left uncoated or top coated with a wide range of finishing paints to further increase protection.
How To Use
Open lever lid cans with care away from face and eyes. electrox can be applied using brush, airless or conventional spray. Ideally apply to steel surfaces prepared to Swedish Standard SA 2.5 (Second Quality BS. 4232) Do not exceed 75 micron surface profile. Stir before and during use – feel for settled zinc powder with stirrer and continue to stir until fully incorporated.
electrox can be used to protect rusted, wire-brushed substrate – remove all loose flaky corrosion deposits. All surfaces must be free of grease, oil and millscale.
Stir product well before and during use.
Ensure all edges are protected. Apply 1 full coat, do not over brush.
For severe, marine duty the application of a second coat after 3 hrs is recommended. Each coat should be applied to WFT (wet film thickness) of 100 microns to achieve around 42 microns DFT (dry film thickness) per coat.
Surface dry 20-30 minutes. Hard Dry 3 hours.
Over coating can be carried out once film is hard dried – but high solvency top coats should be applied after 24 hrs. electrox can be over coated with a wide-range of top coating systems – check compatibility on small scale before use. Where surface is likely to be subject to mechanical impact from debris over coating with stone chip protection is desirable.
Coverage 8-10 sq metres per litre
Thinner if required: xylene.
Also available in 1000ml aerosol